904L奧氏體不鏽鋼為什麼難以加工

摘要：<p class="MsoNormal"> <span lang="EN-US" style="color:#000000;">904L</span><span style="color:#000000;">奧氏體不鏽鋼為什麼難以加工</span> </p> <p class="MsoNormal"> <a href="/timemodel/secondctg/2013-10-26/3147521/1.html" target="_blank"><span lang="EN-US" style="color:#000000;">904L</span><span style="color:#000000;">不鏽鋼</span></a><span style="color:#000000;">的牌號是</span><span lang="EN-US" style="color:#000000;">00Cr20Ni25M04.5Cu</span><span style="color:#000000;">，屬於一種含碳量很低的高合金化的超級奧氏體不鏽鋼。在稀硫酸環境中具備很強的抗腐蝕性，因為銅的添加使它具有很強的抗酸能力，是專為腐蝕條件苛刻的環境而設計。因此這種奧氏體不鏽鋼主要用於抗腐蝕壓力容器的製造。</span> </p> <p class="MsoNormal"> <span lang="EN-US" style="color:#000000;">904L</span><span style="color:#000000;">的成分以鉻、鎳等元素為主，屬於難加工材料，切削加工性較差，主要原因如下。</span><span lang="EN-US"> </span> </p> <p class="MsoNormal"> <span style="color:#000000;">首先是</span><a href="/timemodel/secondctg/2013-10-26/3147521/1.html" target="_blank"><span lang="EN-US" style="color:#000000;">904L</span><span style="color:#000000;">不鏽鋼</span></a><span style="color:#000000;">比彆的種類不鏽鋼，切削力更大。因為</span><a href="/timemodel/secondctg/2013-10-26/3147521/1.html" target="_blank"><span lang="EN-US" style="color:#000000;">904L</span><span style="color:#000000;">不鏽鋼</span></a><span style="color:#000000;">硬度雖然不高</span><span lang="EN-US" style="color:#000000;">(70-90HRB)</span><span style="color:#000000;">，但塑性較好，延伸率</span><span lang="EN-US" style="color:#000000;">≥40</span><span style="color:#000000;">％，斷麵收縮率</span><span lang="EN-US" style="color:#000000;">≥50</span><span style="color:#000000;">％，抗拉強度盯</span><span lang="EN-US" style="color:#000000;">бb≥490MPa</span><span style="color:#000000;">，屈服強度盯</span><span lang="EN-US" style="color:#000000;">б0.2≥216MPa</span><span style="color:#000000;">，因而在切削過程中塑性變形大，使切削力增加。</span> </p> <p class="MsoNormal"> <span style="color:#000000;">其二是導熱係數低。</span><a href="/timemodel/secondctg/2013-10-26/3147521/1.html" target="_blank"><span lang="EN-US" style="color:#000000;">904L</span><span style="color:#000000;">不鏽鋼</span></a><span style="color:#000000;">的熱導率</span><span lang="EN-US" style="color:#000000;">(20</span><span style="color:#000000;">℃時</span><span lang="EN-US" style="color:#000000;">)</span><span style="color:#000000;">為</span><span lang="EN-US" style="color:#000000;">12.9W</span><span style="color:#000000;">／</span><span lang="EN-US" style="color:#000000;">(mmK)</span><span style="color:#000000;">，導熱係數低，隻有</span><span lang="EN-US" style="color:#000000;">45</span><span style="color:#000000;">鋼的</span><span lang="EN-US" style="color:#000000;">1</span><span style="color:#000000;">／</span><span lang="EN-US" style="color:#000000;">4</span><span style="color:#000000;">左右</span><span lang="EN-US" style="color:#000000;">(45</span><span style="color:#000000;">鋼的熱導率為</span><span lang="EN-US" style="color:#000000;">47.5W</span><span style="color:#000000;">／</span><span lang="EN-US" style="color:#000000;">(mmK))</span><span style="color:#000000;">。導熱性是影響切削熱傳導的主要因素之一，被加工材料的導熱性越低，由切屑和工件帶走的熱量就愈少，而刀具上積聚的熱量就越多，使刀具極易磨損。</span> </p> <p class="MsoNormal"> <span style="color:#000000;">其三是容易形成積屑瘤。由於</span><span lang="EN-US" style="color:#000000;">904L</span><span style="color:#000000;">不鏽鋼韌性大，所以在切削過程中與刀具材料的親和力強，切削時刀具的前刀麵與切屑底層金屬發生強烈摩擦，在高溫高壓的作用下會產生粘附現象，生成積屑瘤，不易獲得表麵粗糙度要求高的加工表麵。</span> </p> <p class="MsoNormal"> <span style="color:#000000;">其四是切屑不易彎曲折斷，</span><span lang="EN-US" style="color:#000000;">904L</span><span style="color:#000000;">不鏽鋼的材料延伸率高，所以在切削過程中切屑不易彎曲而折斷。如果不采取適當措施，會影響切削過程的正常進行，而且容易劃傷已加工表麵，甚至還會使刀具崩刃和損壞。</span> </p> <p class="MsoNormal"> <span style="color:#000000;">因為</span><a href="/timemodel/secondctg/2013-10-26/3147521/1.html" target="_blank"><span lang="EN-US" style="color:#000000;">904L</span><span style="color:#000000;">不鏽鋼</span></a><span style="color:#000000;">的上述特點，在用常規刀具和傳統方法對其進行切削時，即使選擇非常小的切削用量，刀具仍然極易磨損，加工效率低，且工件很難達到圖樣所要求的表麵粗糙度和加工精度。</span> </p> <p class="MsoNormal"> <span lang="EN-US"> </span> </p>